ABSTRACT
This study compared the surface roughness and microbial adhesion characteristics of Omnichroma, a novel composite resin developed using “smart chromatic technology”, with those of two other conventional composite resins with different filler compositions. A total of 144 specimens were fabricated using 3 types of composite resins: Omnichroma (nano-spherical), Filtek Z350XT (nanofill), and Tetric N-Ceram (nanohybrid) and, divided into 3 groups of 48. Finishing was performed using tungsten carbide burs. Specimens were then divided into 3 subgroups using different polishing methods: Control, SofLex, and PoGo. Surface roughness was analyzed quantitatively and qualitatively using an atomic force microscope and a scanning electron microscope. Microbial adhesion was assessed by culturing Streptococcus mutans on the specimens for 24 hours and then measuring colony-forming units attached to the upper surface. The surface roughness (Ra) of Omnichroma was 0.123 μm after finishing, and it exhibited a smooth surface compared to the other resins. However, after polishing, there were no significant differences in the surface roughness between the three composite groups, regardless of the polishing methods. The surfaces of the Control subgroups were significantly rougher than those of the SofLex subgroups in all 3 composite groups. However, except for Tetric N-Ceram, there were no significant differences between the Control and PoGo subgroups in the other composite groups. Microbial adhesion assessment showed no significant differences between any of the 3 composite resin subgroups; however, Omnichroma exhibited higher microbial adhesion than the other two composites. No significant correlation was observed between surface roughness and microbial adhesion.
ABSTRACT
Restoring composite resins with the optimal shades for all primary teeth is a great challenge for pediatric dentists. A newly developed single-shade composite resin can exhibit a color similar to that of the surrounding tooth structure based on the structural color phenomenon. This study aims to evaluate the color adjustment potential (CAP) of a single-shade composite resin compared to conventional multi-shade composite resins in primary teeth. A single-shade composite resin and two conventional multi-shade composite resins were included in this study. Two types of specimens, a single specimen and a dual specimen, were evaluated. For single specimens, duplications of the primary second molar denture teeth were made using experimental composite resins. For dual specimens, cavities were prepared on the buccal surfaces of extracted primary second molars and restored with experimental composite resins. The L*, a*, and b* values were measured using a colorimeter for the extracted teeth and specimens. The mean ΔEab* values for single and dual specimens and CAP were calculated. Bonferroni post-hoc analysis was performed to confirm the statistical significance between the ΔEab* and CAP values of the experimental resins. Among the single specimens, the single-shade composite resin showed significantly higher ΔESingle compared to other composite resins (p < 0.0167). There was no significant difference between ΔEDual for all experimental resins. The single-shade composite resin showed highest CAP compared to other multi-shade composite resins. A single-shade composite resin exhibited the most prominent color adaptability compared to other conventional multi-shade composite resins for primary second molars. A single-shade composite resin can simplify shade matching and provide esthetic outcomes for the restoration of primary second molars.
ABSTRACT
This study aimed to evaluate the effect of silver diamine fluoride (SDF) and potassium iodide (KI) on the formation of cariogenic biofilm and surface roughness in vitro. A total of 48 bovine dentin specimens with artificially induced caries were prepared and divided into 3 groups of 16: untreated control, SDF-treated, and SDF-treated followed by KI (SDFKI). Ten specimens from each group were used to observe microbial adhesion. Multispecies cariogenic biofilms including Streptococcus mutans , Lactobacillus casei , and Candida albicans were cultured on the specimens. Microbes were cultured for 24 hours, and the colony-forming unit was calculated. The remaining specimens were observed by atomic force microscope and scanning electron microscope (SEM). The number of bacteria was significantly lower in the SDF and SDFKI groups. KI did not inhibit the antibacterial activity of SDF significantly. SEM images showed particles generated after SDF and SDFKI application were deposited on the dentin, but there was no significant difference in surface roughness between the 3 groups. This study confirmed that SDF and SDFKI application did not have a significant effect on the surface roughness of dentin, but effectively inhibited the formation of the early cariogenic bacterial film after 24 hours compared to the control.
ABSTRACT
This study evaluated the fluoride release of alkasite restorative material (ARM) and giomer penetrating the dentin adhesive layer.Twenty specimens were prepared for each restorative material, and dentin adhesive with uniform thickness was applied to half of them. The prepared specimens were placed in a polyethylene tube containing 2.0 mL of deionized water and deposited in a 37.0°C water bath for the study duration. The amount of fluoride release was measured on the 1st, 3rd, 7th, 14th, 21st, and 28th days after deposition.The dentin adhesive applied to the ARM and giomer could not completely block the fluoride release; however, it significantly reduced its amount. The cumulative amount of fluoride release of the ARM after 28 days was higher than that of the giomer regardless of the application of dentin adhesive.